MAX CLR Top Coat
For ordering and inquiries please call 877-403-8008.
Or visit our eBay Store.
PolymerProducts on eBay
Available Kit Sizes:
Description
It offers excellent mechanical performance while maintaining crystal clarity, high gloss finish low air bubble entrapment superior aesthetic qualities of the coating.
Its none blushing performance, high gloss finish, excellent transparent clarity, color stability and ease of use make MAX CLR-TC an excellent choice for protective and aesthetic coatings with excellent aesthetic cured performance. MAX CLR-TC also offers high chemical resistance, structural adhesion and overall durability suitable for many protective coatings applications.
MAX CLR-TC A/B performs well at room temperature use and can withstand cyclic exposure to temperatures form -40°C to 112°C with minimal loss of mechanical performance. Upon Cure, MAX CLR-TC A/B resists extreme and repeated thermal shocks
making it well suited for bonding substrates with dissimilar expansion coefficients.
MAX CLR-TC A/B can be as as an adhesive for bonding at variety of substrates such as composite materials, concrete and ceramic products, plastics, wood, glass, steel,aluminum and most soft metals.
Physical and Mechanical Properties
| Density | 1.10 G/CC |
| Form and Color | Clear Liquid |
| Viscosity | 1,125 cPs @ 25ºC Mixed |
| Mix Ratio | 50 Parts “B” to 100 Parts “A” By Weight |
| Working Time | 45 – 50 Minutes @ 25ºC(100 Gram Mass) |
| Peak Exotherm | 70ºC (100 Gram Mass) |
| Thin Film Set Time (dry to the touch) | 4 to 6 Hours |
| Handle Time | 8 Hours |
| Cure Time And Accelerated Cure Time | 2 to 7 days @ 25ºC or 8 hours at room temperature plus 1 hours at 100ºC |
| Hardness | 75 ± 5 Shore D, |
| Tee-Peel Strength | 3.7 Lbs. per inch Width |
| Tensile Shear Strength | 2,554 psi @ 25ºC |
| 1,010 psi @ -40ºC | |
| 950 psi @ 100ºC | |
| Elongation | 3.0% @ 25ºC |
| Flexural Strength | 13,000 psi |
| Flexural Modulus | 344,000 psi |
| Heat Deflection Temp. | 110ºC |
Chemical Resistance Performance
Full Immersion at 30°C
Measured Percent Changes in Weight
| REAGENT | 3 days | 28 days |
| Deionized Water | 0.32 | 1.50 |
| Sea Water | 0.10 | 0.98 |
| Methanol | 7.93 | -2.41 |
| Ethanol | 3.98 | 10.28 |
| Toluene | 0.54 | 2.86 |
| Xylene | 0.34 | 0.05 |
| Butyl Cellosolve | 16.63 | 5.31 |
| MEK | Destroyed | Destroyed |
| 10% Lactic Acid | 1.21 | 5.42 |
| 10% Acetic Acid | 0.54 | 0.45 |
| 70% Sulfuric Acid | 0.08 | 0.14 |
| 50% Sodium Hydroxide | 0 | 0 |
| 10% Sodium Hypochlorite | 0.51 | 1.36 |